E058-3
| Product Name | E058-3 |
| Product Type | POE-g-MAH |
| Appearance | Colorless to semi-translucent yellowish granules |
| Density (g/cm³) | 0.87±0.02 |
| Melting Point (℃) | 66 |
| [1] MFR (g/10min) | ≥0.2 |
| [2] Grafting Ratio | Very High |
| Dosage | 2-15% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Introduction
E058-3 is a high-performance elastomer graft modifier tailored for nylon (PA) and TPE soft rubber systems. With extremely low hardness (about 55A) and 15–20% higher toughness than similar products, it’s especially suitable for low-temperature toughening of modified nylon and TPE soft rubber overmolding. Its unique molecular structure improves impact resistance while retaining excellent soft touch, effectively balancing the mechanical strength and processing adaptability of products—an ideal choice for engineering plastics and TPE soft rubber composites in low-temperature environments.
application
1、PA, TPE toughening overmolding systems,
2、PA/PP alloy systems,
3、PA reinforcement, toughening, filling, and flame-retardant systems.
related parameters
| Product Name | E058-3 |
| Product Type | POE-g-MAH |
| Appearance | Colorless to semi-translucent yellowish granules |
| Density (g/cm³) | 0.87±0.02 |
| Melting Point (℃) | 66 |
| [1] MFR (g/10min) | ≥0.2 |
| [2] Grafting Ratio | Very High |
| Dosage | 2-15% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Packaging and Storage
25 KG kraft paper bags with inner plastic liners.
Store in dry, ventilated, cool conditions (≤25°C). Avoid humidity and direct sunlight. Use promptly after opening.