| Product Name | E058-P |
| Product Type | POE-g-MAH |
| Appearance | Colorless to semi-translucent yellowish granules |
| Density (g/cm³) | 0.87±0.02 |
| Melting Point (℃) | 66 |
| [1] MFR (g/10min) | ≥0.5 |
| [2] Grafting Ratio | High |
| Dosage | 3-20% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Introduction
E058-P is a high-performance elastomer graft compatibilizer for nylon (PA) toughening modification. With high toughness, excellent fluidity, and strength, it significantly improves product surface finish and scratch resistance while maintaining cost advantages. Its environmentally friendly formula is odorless with a low addition amount. Through high grafting rate technology, it realizes efficient toughening and adopts a unique black-spot control process. The product is widely applied in glass fiber-reinforced toughened PA, toughened nylon ties/pipes, flame-retardant systems, and nylon sheet processing, having both barrier properties and surface texture—an ideal choice for engineering plastics reinforcement, toughening, and environmentally friendly products.
application
1、Fiberglass -reinforced toughened PA;
2、Flame-retardant reinforced toughened PA;
3、Toughened nylon, nylon ties, nylon pipes;
4、Nylon sheets.
related parameters
| Product Name | E058-P |
| Product Type | POE-g-MAH |
| Appearance | Colorless to semi-translucent yellowish granules |
| Density (g/cm³) | 0.87±0.02 |
| Melting Point (℃) | 66 |
| [1] MFR (g/10min) | ≥0.5 |
| [2] Grafting Ratio | High |
| Dosage | 3-20% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Packaging and Storage
25 KG kraft paper bags with inner plastic liners.
Store in dry, ventilated, cool conditions (≤28°C). Avoid humidity and direct sunlight. Use promptly after opening.