E018-9H
| Product Name | E018-9H |
| Product Type | HDPE-g-MAH |
| Appearance | Transparent or semi-translucent granules |
| Density (g/cm³) | 0.95±0.01 |
| Melting Point (℃) | 125 |
| [1] MFR (g/10min) | ≥0.1 |
| [2] Grafting Ratio | High |
| Dosage | 2-8% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Introduction
E018-9H is a formulated maleic anhydride-grafted high-density polyethylene (HDPE-g-MAH) composite. Widely used in wood-plastic and bamboo-plastic composites, it offers exceptional compatibility between polyolefin resins and bio-based fibers. As a high-performance compatibilizer, it is also suitable for PE/PA alloy systems and overmolding processes involving TPE and PA-based materials (e.g., glass-fiber-reinforced nylon or PA6 wood-plastic systems). Its key advantages include superior interfacial adhesion, high impact strength, long-term bonding performance, and recyclability, significantly enhancing the mechanical properties and processing stability of composites.
application
1、Wood-plastic composites (WPC), bamboo-plastic composites (BPC),
2、PA modification,
3、TPE overmolding,
4、PA/HDPE alloy systems.
related parameters
| Product Name | E018-9H |
| Product Type | HDPE-g-MAH |
| Appearance | Transparent or semi-translucent granules |
| Density (g/cm³) | 0.95±0.01 |
| Melting Point (℃) | 125 |
| [1] MFR (g/10min) | ≥0.1 |
| [2] Grafting Ratio | High |
| Dosage | 2-8% |
| Packaging | 25KG Bag |
| Delivery Time | 10 Working Days |
Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.
Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.
Notes:
[1] MFR measured at 190°C, 2.16 kg load.
[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.
Packaging and Storage
25 KG kraft paper bags with inner plastic liners.
Store in dry, ventilated, cool conditions (≤30°C). Avoid humidity and direct sunlight. Use promptly after opening.