E058-Si

Introduction

The E058-Si system modifies and grafts ethylene-octene copolymer (POE) via a special process, significantly enhancing the affinity and adhesion between resins, as well as between resins and inorganic substances (e.g., glass), thus improving peel and tear strength. With odorless environmental protection features, it optimizes the processing environment to meet eco-friendly and export standards. Boasting higher grafting efficiency, lower addition amount, and unique grafting & crystal point control processes, it holds broad application prospects in the photovoltaic industry.    

application

1、Photovoltaic films: Optimize photovoltaic film system performance, boost interlayer bonding, reduce aging delamination risks.
2、Glass/fiberglass bonding systems: Strengthen adhesion between glass, fiberglass and other materials, ensure composite system structural stability.    

related parameters

Disclaimer: Data provided is based on internal laboratory testing and serves as a reference for material selection. It shall not be construed as product specifications.

Testing Limitations: Due to limited data and experience, the above performance metrics are for reference only.   

Notes:

[1] MFR measured at 190°C, 2.16 kg load.

[2] Grafting ratio classification: Ultra high: >1.8% | Very High: 1.0–1.2% | High: 0.8–1.0% | Moderately high: 0.5–0.8% | Medium: ≈0.5%.

Packaging and Storage    

25 KG kraft paper bags with inner plastic liners.
Store in dry, ventilated, cool conditions (≤25°C). Avoid humidity and direct sunlight. Use promptly after opening.